Carburization Prevention Treatment,Process 1:202 Coating Material
To avoid Carburization brittleness,which may occur during pipe casting and which can result in fracture of cooling water pipes with repeated expansion when heated up and contraction when cooled down during service,carburization prevention treatment must be done on water pipes.
1 The main material is metal oxide,green color.
2 Treating method:spray coating ,brush coating or dip coating,at low cost.
3 Coating thickness:0.2~0.3mm.
4 Carburization prevention effect:
Chemical analysis:average carburization≤0.08% within the range of 1mm depth.
Metallurgical analysis:no eutectoid steel layer.
Gap between water pipe and the mother material≤0.12mm
Water pipe tensile strength:#10 steel≥300MPa
#20 steel≥400MPa
Water pipe elongation:#10 steel≥26%
#20 steel≥23%
Cast Iron Stave Cooler, Water-Cooling Converter Mouth, Cast Iron Tuyere Cooler, Cast Copper Tuyere Cooler, Chequer supports, Cast Iron Water Jaker stave cooler cooling stave cast iron stave cooler blast furnace stave cooler blast furnace cooling stave cast iron cooling stave
Reliable Delivery for Formosa Vietnam | Transparent Production, Real Results
From Challenge to Collaboration: A Real Case of International Foundry Partnership
In metallurgical cooling equipment, there’s no single answer — only the right process for each part.
How We Deliver Reliability — One Package at a Time